Stainless Steel, AISI 316L Material Information
Specifications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 79 | 79 | |
| Tensile Strength, Ultimate | 560 MPa | 81200 psi | |
| Tensile Strength, Yield | 290 Mpa | 42100 psi | |
| Elongation at Break | 50% | 50% | In 50 mm |
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| Charpy Impact | 103 J | 76 ft-lb | V-notch, 30°C |
| Izod Impact | 150 J | 111 ft-lb | 21°C, 150 J at -195°C (-320°F) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 7.4e-005 ohm-cm | 7.4e-005 ohm-cm | at 20°C |
| Magnetic Permeability | 1.008 | 1.008 | at RT |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.5 J/g-°C | 0.12 BTU/lb-°F | from 0-100°C (32-212°F) |
| Melting Point | 1375 – 1400°C | 2510 – 2550°F | |
| Solidus | 1375°C | 2510°F | |
| Liquidus | 1400°C | 2550°F | |
| Maximum Service Temperature, Air | 870°C | 1600°F | Intermittent Service |
| Maximum Service Temperature, Air | 925°C | 1700°F | Continuous Service |
NOTE: The information in this data sheet is for design guidance only. Forming methods and specific geometry could affect properties.
Overview
Austenitic stainless steel has excellent corrosion resistance and elongation. Non-magnetic. Easily weldable. Can be polished to a mirror finish. Provides better elongation and ductility over the “standard” grade. This alloy can be milled into coils, sheets, plates, bars, wire, and tubing. Often used for food industry, marine, medical, and applications where corrosion resistance is of higher importance over that of strength or wear resistance. Data provided by Mead Metals and MatWeb.com.
Applications & Usage
- Mounting Plates
- Gas Feed Tubes
- Vaporizer Nozzles
- Fasteners, Springs & Retainer Pins
- MESC Flange Inserts
- Hemostats
- Surgical Implants
- Bridges
- Kitchen accessories, cutlery and cookware
- Auto Bodies
- Aircraft
Industries Using This Material
- Semiconductor
- Medical
- Food